This study presents a methodology for producing high-strength aluminium alloy powders through in situ alloying within the melting crucible combined with ultrasonic atomization. Pure elemental feedstock was melted, alloyed, and homogenized using electromagnetic stirring induced by an alternating magnetic field and enhanced by argon gas injection. The resulting powder was characterized and subsequently validated for Laser Powder Bed Fusion (LPBF). Test specimens were fabricated and mechanically characterized to evaluate the printability and performance of the developed alloy. The results demonstrate the feasibility of integrating alloy design, powder production, and additive manufacturing into a single, streamlined process route.
Alligazione in situ e atomizzazione ultrasonica per lo sviluppo di polveri di leghe di alluminio ad alta resistenza destinate alla Laser Powder Bed Fusion (LPBF)
Questo studio presenta una metodologia per la produzione di polveri di leghe di alluminio ad alta resistenza mediante alligazione in situ all’interno del crogiuolo di fusione, combinata con l’atomizzazione ultrasonica. Materie prime elementari pure sono state fuse, legate e omogeneizzate mediante agitazione elettromagnetica indotta da un campo magnetico alternato e potenziata dall’iniezione di gas argon. La polvere ottenuta è stata caratterizzata e successivamente validata per la Laser Powder Bed Fusion (LPBF). Sono stati realizzati provini di prova e sottoposti a caratterizzazione meccanica per valutare la stampabilità e le prestazioni della lega sviluppata. I risultati dimostrano la fattibilità di integrare la progettazione della lega, la produzione della polvere e la manifattura additiva in un unico processo integrato.
more info: https://www.simusrl.com/
https://www.simusrl.com/digital_manufacturing/3dlab/